Custom Titanium Forging
Custom Titanium Forging supplied by titanium grade, governing specification, dimensions or drawing, melt/forging route, condition, inspection and traceability requirements.
- Grades
- Commercially pure and alloy titanium as specified
- Standard
- ASTM B381 / ASME SB381, AMS or approved customer specification
- Form
- Drawing-specific open-die or near-net forging
- Documents
- MTC, heat/lot traceability and agreed inspection reports
Product Detail
Product Introduction
Custom Titanium Forging is drawing-specific open-die or near-net forging supplied for further processing or finish machining. Grade, specification, melt or forging route, section size, heat treatment, machining allowance and inspection must be defined before production review.
Product Specifications
| Product | Custom Titanium Forging | Grade | Commercially pure or alloy titanium as specified |
|---|---|---|---|
| Standard | ASTM B381 / ASME SB381, AMS or approved customer specification may govern the product where applicable. Aerospace and critical-service orders may invoke an AMS or customer specification with additional melt, forging, heat-treatment, sampling and inspection requirements. | Size & Form | Drawing-specific open-die or near-net forging by drawing, diameter/section, length, weight and machining allowance |
| Tolerance | Applicable specification and order-defined dimensions, weight, crop, straightness, allowance and surface requirements | Supply Condition | As-cast, rough turned, forged, annealed, heat treated, descaled, rough machined or finish machined as agreed |
| Inspection | Melt and heat traceability, certificate and chemistry review, dimensions and weight, surface/crop condition, heat treatment, mechanical testing, macrostructure or microstructure and ultrasonic testing when specified. | Documents | MTC, heat/lot traceability and agreed inspection reports |
Send the complete material RFQ
Include grade, specification revision, dimensions, tolerance, quantity, condition, tests and destination.
Chemical Composition
Weight percent; maximum unless a range is shown. Titanium is the balance. The ordered specification and grade control.
| Grade / UNS | Principal Alloying Elements | Fe max | O max | C max | N max | H max | Ti |
|---|---|---|---|---|---|---|---|
| Grade 1 / R50250 | — | 0.20 | 0.18 | 0.08 | 0.03 | 0.015 | Balance |
| Grade 2 / R50400 | — | 0.30 | 0.25 | 0.08 | 0.03 | 0.015 | Balance |
| Grade 3 / R50550 | — | 0.30 | 0.35 | 0.08 | 0.05 | 0.015 | Balance |
| Grade 4 / R50700 | — | 0.50 | 0.40 | 0.08 | 0.05 | 0.015 | Balance |
| Grade 5 / R56400 | Al 5.50–6.75; V 3.50–4.50 | 0.40 | 0.20 | 0.08 | 0.05 | 0.015 | Balance |
| Grade 6 / R54520 | Al 4.00–6.00; Sn 2.00–3.00 | 0.50 | 0.20 | 0.08 | 0.05 | 0.015 | Balance |
| Grade 7 / R52400 | Pd 0.12–0.25 | 0.30 | 0.25 | 0.08 | 0.03 | 0.015 | Balance |
| Grade 9 / R56320 | Al 2.50–3.50; V 2.00–3.00 | 0.25 | 0.15 | 0.08 | 0.03 | 0.015 | Balance |
| Grade 12 / R53400 | Mo 0.20–0.40; Ni 0.60–0.90 | 0.30 | 0.25 | 0.08 | 0.03 | 0.015 | Balance |
| Grade 11 / R52250 | Pd 0.12–0.25 | 0.20 | 0.18 | 0.08 | 0.03 | 0.0125 | Balance |
| Grade 16 / R52402 | Pd 0.04–0.08 | 0.30 | 0.25 | 0.08 | 0.03 | 0.015 | Balance |
| Grade 17 / R52252 | Pd 0.04–0.08 | 0.20 | 0.18 | 0.08 | 0.03 | 0.0125 | Balance |
| Grade 19 / R58640 | Al 3.00–4.00; V 7.50–8.50; Cr 5.50–6.50; Mo 3.50–4.50; Zr 3.50–4.50 | 0.30 | 0.12 | 0.05 | 0.03 | 0.015 | Balance |
| Grade 23 / R56407 | Al 5.50–6.50; V 3.50–4.50 | 0.25 | 0.13 | 0.08 | 0.05 | 0.0125 | Balance |
Mechanical Properties – Annealed Material Reference
| Grade | Ultimate Tensile Strength min | 0.2% Yield Strength min | Elongation min |
|---|---|---|---|
| Grade 1 | 240 MPa | 170 MPa | 24% |
| Grade 2 | 345 MPa | 275 MPa | 20% |
| Grade 3 | 450 MPa | 380 MPa | 18% |
| Grade 4 | 550 MPa | 483 MPa | 15% |
| Grade 5 | 895 MPa | 828 MPa | 10% |
| Grade 6 | 828 MPa | 793 MPa | 10% |
| Grade 7 | 345 MPa | 275 MPa | 20% |
| Grade 9 | 620 MPa | 485 MPa | 15% |
| Grade 12 | 483 MPa | 345 MPa | 18% |
| Grade 11 | 240 MPa | 170 MPa | 24% |
| Grade 16 | 345 MPa | 275 MPa | 20% |
| Grade 17 | 240 MPa | 170 MPa | 24% |
| Grade 19 / Beta-C | Acceptance depends on solution treatment, aging condition, product form and section size; use the certified values required by the invoked product or aerospace specification. | ||
| Grade 23 | 860 MPa | 795 MPa | 10% |
Representative minima only. Product form, section size, heat treatment and the invoked specification determine the certified acceptance values.
Typical Physical Properties
| Grade | Density | Elastic Modulus | Thermal Expansion |
|---|---|---|---|
| Grade 1 | 4.51 g/cm³ | Approx. 103 GPa | Approx. 8.6 µm/m·K |
| Grade 2 | 4.51 g/cm³ | Approx. 105 GPa | Approx. 8.6 µm/m·K |
| Grade 3 | 4.51 g/cm³ | Approx. 105 GPa | Approx. 8.6 µm/m·K |
| Grade 4 | 4.51 g/cm³ | Approx. 105 GPa | Approx. 8.6 µm/m·K |
| Grade 5 | 4.43 g/cm³ | Approx. 114 GPa | Approx. 8.6 µm/m·K |
| Grade 6 | Approx. 4.48 g/cm³ | Approx. 110 GPa | Approx. 8.8 µm/m·K |
| Grade 7 | Approx. 4.51 g/cm³ | Approx. 105 GPa | Approx. 8.6 µm/m·K |
| Grade 9 | Approx. 4.48 g/cm³ | Approx. 105 GPa | Approx. 9.0 µm/m·K |
| Grade 12 | Approx. 4.54 g/cm³ | Approx. 103 GPa | Approx. 8.6 µm/m·K |
| Grade 11 | Approx. 4.51 g/cm³ | Approx. 103 GPa | Approx. 8.6 µm/m·K |
| Grade 16 | Approx. 4.51 g/cm³ | Approx. 105 GPa | Approx. 8.6 µm/m·K |
| Grade 17 | Approx. 4.51 g/cm³ | Approx. 103 GPa | Approx. 8.6 µm/m·K |
| Grade 19 / Beta-C | Approx. 4.82 g/cm³ | Condition-dependent; use certified engineering data | Condition-dependent; verify for design |
| Grade 23 | 4.43 g/cm³ | Approx. 114 GPa | Approx. 8.6 µm/m·K |
Typical engineering references, not inspection acceptance limits.
Certificates & Inspection Records
Services We Can Provide
Product Packaging
Blocks and forgings are protected at machined surfaces, secured on pallets or in export cases, and identified by grade, heat, dimensions and quantity.
Application Scenarios
Custom rings, hubs, discs, blocks and asymmetric near-net industrial components
Material grade, dimensions, condition and inspection must be matched to the application requirements.
Aerospace, marine and chemical equipment
Material grade, dimensions, condition and inspection must be matched to the application requirements.
Heavy-duty machined titanium components
Material grade, dimensions, condition and inspection must be matched to the application requirements.
FAQ
Which product specification should be stated?
Use the specification that covers the exact ingot, billet or forging form, grade and service; critical orders may require additional AMS or customer controls.
Why must machining allowance be defined?
Forging and primary stock need sufficient cleanup allowance for the finished part without unnecessary titanium weight and machining cost.
What information is required for quotation?
Provide grade, specification, drawing or dimensions, quantity/weight, route, condition, allowance, testing and certificates.
Leave Your Message
Related Technical Guides
Titanium Ingot, Billet and Forging Guide
Understand material route and inspection.
Read technical guideForgings vs Machined-from-Bar
Compare stock route and performance.
Read technical guideTitanium RFQ Checklist
Prepare grade, dimensions and documentation.
Read technical guide