Grade 5 Titanium Fender Washers
Grade 5 Titanium Fender Washers with large outside diameters for distributing bearing load over thin, slotted or soft mating materials. Dimensions, condition, working requirement and inspection follow the approved order.
- Material
- Grade 5 / Ti-6Al-4V / UNS R56400
- Form
- Flat washer with enlarged outside diameter
- Dimensions
- Metric, inch or approved drawing
- Documents
- MTC and dimensional inspection
Product Detail
Product Introduction
Grade 5 Titanium Fender Washers are flat washers with a relatively large outside diameter compared with the bolt hole. They spread bearing load over a wider area, but plate bending, washer dishing, edge distance, hole clearance and mating-material strength must be checked for the complete joint.
Product Specifications
| Product | Grade 5 Titanium Fender Washers | Material | Titanium Grade 5 / Ti-6Al-4V / UNS R56400 |
|---|---|---|---|
| Product Form | Flat, split-lock or drawing-specific washer | Typical Inquiry Range | For M2 to M36 fasteners in typical inquiries; custom ID, OD and thickness by review |
| Dimensional References | ISO 7089/7090, DIN 125, ASME B18.21 or approved drawing | Threads / Dimensions | Metric coarse or fine, UNC, UNF or drawing-specific as applicable |
| Surface | Machined and cleaned; lubricant, anti-galling treatment or coating by agreement | Documents | MTC, heat/lot traceability and dimensional inspection report |
| Inspection | Dimensions, thread gauging, surface and agreed functional or mechanical tests | Supply Basis | Approved purchase order, invoked standard and drawing |
Typical inquiry ranges are not a stock guarantee. Final manufacturability, tolerances and test requirements are confirmed against the complete RFQ.
Selection and Configuration
- Bearing area: Choose OD and thickness from the mating material, hole or slot size, edge distance and required bearing stress.
- Hole and fit: Define inside diameter and clearance for the fastener without allowing excessive eccentric loading.
- Stiffness and seating: Confirm washer flatness, thickness and support so the large washer does not dish or bridge an uneven surface.
Send a drawing or complete fastener definition
Include dimensions, quantity, mating parts, service conditions, finish and inspection requirements.
Chemical Composition – Titanium Grade 5
Weight percent. Values are material limits; titanium is the balance.
| Al | V | Fe max | O max | C max | N max | H max | Residual each / total | Ti |
|---|---|---|---|---|---|---|---|---|
| 5.50–6.75 | 3.50–4.50 | 0.40 | 0.20 | 0.08 | 0.05 | 0.015 | 0.10 / 0.40 | Balance |
Mechanical Properties – Grade 5 Material Reference
| Property | Annealed Grade 5 Material Reference Minimum |
|---|---|
| Ultimate tensile strength | 895 MPa (130 ksi) |
| 0.2% yield strength | 828 MPa (120 ksi) |
| Elongation | 10% |
| Reduction of area | 25% |
Material values do not automatically establish finished-fastener loadability. Finished-part acceptance depends on geometry, manufacturing route, condition and the expressly invoked fastener specification or drawing.
Typical Physical Properties
| Property | Typical Value |
|---|---|
| Density | 4.43 g/cm³ |
| Elastic modulus | Approximately 114 GPa |
| Poisson ratio | Approximately 0.34 |
| Thermal conductivity | Approximately 6.7 W/m·K |
| Coefficient of thermal expansion | Approximately 8.6 µm/m·K |
| Melting range | Approximately 1604–1660°C |
Physical values are typical engineering references and are not inspection acceptance limits.
Certificates & Inspection Records
Services We Can Provide
Product Packaging
Grade 5 Titanium Fender Washers are separated by size and lot, protected against thread and surface damage, and labeled with grade, dimensions, quantity and traceability reference. Inner bags, cartons and export cases are selected according to product geometry, quantity and shipping method.
Application Scenarios
Chemical Processing
Corrosion-resistant equipment joints selected against the complete process environment.
Power & Energy
Lightweight engineered assemblies requiring controlled dimensions and traceability.
Marine & Shipbuilding
Corrosion-resistant joints subject to galvanic, preload and service-condition review.
FAQ
Why use a fender washer instead of a standard flat washer?
Its larger OD distributes bearing load over more area and can bridge an oversized or slotted hole, subject to plate and washer stiffness checks.
Does a larger OD always improve the joint?
No. Insufficient thickness or uneven support can cause dishing or bending, and nearby edges can limit effective bearing area.
What dimensions should be stated?
Provide bolt size or ID, washer OD, thickness, flatness and edge requirements, quantity, mating material, tests and certificates.
Leave Your Message
Related Technical Guides
Titanium Fastener Selection Guide
Define washer function, geometry and inspection.
Read technical guideHow to Prevent Galling
Review mating surfaces and installation.
Read technical guideTitanium Fasteners for Marine Applications
Review corrosion and joint materials.
Read technical guide